1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
چسبندگی کمربند مقاوم در برابر دمای بالا بوم پنبه نسبتا کم است و چسبندگی کمربند مقاوم در برابر دمای بالا EP نسبتاً زیاد است. طول عمر کمربند مقاوم در برابر دمای بالا EP آشکارا طولانی تر از کمربند مقاوم در برابر دمای بالا بوم پنبه است.
3. Hot glue stripping method (is it good to remove the glue at one end)?
این یکی دیگر از روش های چسباندن است، این روش نیز امکان پذیر است، اما اگر از این روش استفاده می کنید به نکات زیر توجه کنید:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
معمولاً هنگامی که دمای ولکانیزاسیون بالاتر از دمای بحرانی ولکانیزاسیون شتاب دهنده و عامل ولکانیزاسیون است و نمی تواند به دمای طبیعی ولکانیزه برسد، می توان روش طولانی کردن زمان ولکانیزاسیون را اتخاذ کرد تا ولکانیزاسیون لاستیک مطابق با الزامات باشد. به طور کلی، هر بار که دما کمتر از 10 درجه باشد، زمان ولکانیزاسیون 2-4 برابر افزایش می یابد. البته، به دلایل عملکرد، استفاده از ولکانیزاسیون در دمای پایین و طولانی مدت را توصیه نمی کنیم.
5. Can core rubbers from different manufacturers be mixed?
مخلوط کردن لاستیک هسته از تولید کنندگان مختلف توصیه نمی شود زیرا فرمول لاستیک هسته از تولید کنندگان مختلف متفاوت است. انواع مختلفی از ترکیبات در لاستیک وجود دارد و برخی از آنها واکنش های متقابلی دارند. در فرمول همان سازنده، هیچ ترکیب کننده ای با واکنش های متقابل نامطلوب وجود نخواهد داشت، اما فرمول های سازنده های مختلف بسیار متفاوت است. هنگام استفاده، ممکن است بازتاب های تعاملی عوامل ترکیب کننده وجود داشته باشد که بر اثر استفاده از لاستیک هسته تأثیر می گذارد.